【Product Name】Super Soft Smooth and Clear Silicone Oil RH-NB-8608

【Introduction】 This product is a kind of linear multivariate copolymerization block modification of organic silicon softener

【Advantage】 

(1)Soft, smooth, clear handle feeling;

(2)Do not need emulsifier;

【Basic Character】

Appearance:Light yellow transparent liquid

Ionic:Weak Cationic

Solid content:56%—58%（105℃,3hours）

【Application】

Suitable for all kinds of polyester and cotton fabric

【Usage amount for reference 】 

Dilute method: see next page

(1)Dipping Process: Dilution   1~5 %( o.w.f)

(2)Padding Process: Dilution   10~50g/l

【Package】50KG/Drum, 120KG/Drum, 190KG/Drum, 950KG/Drum.

【Storage】Store in cool, ventilated warehouse, 6 months of storage expiry.

Dilute method

RH-NB-8608：100KG

Glacial acetic acid: 2KG

Water: 300Kg

Emulsion is semi-milky appearance

Dilute process:

1.Add RH-NB-8608 to reactor, start stirring;

2.Add 10Kg water to stir for 5 minutes;

3.Add 10Kg water to stir for 5 minutes;

4.Add 10Kg water to stir for 5-10 minutes, add 2kg glacial acetic acid to stir for 5 minutes;

5.Add 10Kg water to stir for 5 -10minutes;

6.Add 10Kg water to stir for 5-10 minutes, add 5kg acid water to stir for 5minutes;

7.Add 10Kg water to stir for 5 -10minutes;

8.Add 10Kg water to stir for 5 -10minutes;

9.Add 10Kg water to stir for 5 -10minutes;

10.Add 20Kg water to stir for 5 minutes;

11.Add 20Kg water to stir for 5 minutes;

12.Add 50Kg water to stir for 2-3minutes;

13.Slowly add rest water while stirring, add glacial acetic acid to adjust PH value to 6

Notice: Must use high speed machine, last time can add water slowly. Should scrape the reactor side, avoid oil stick on reactor side without fully emulsification.